Deringer-Ney manufactures custom-designed Probes solutions in state-of-the-art manufacturing facilities, delivering greater value at a lower cost. Our alloys uniquely provide increased performance for increased probe reliability even during high temperatures and increased workloads. As an ISO-certified manufacturer and leading alloy developer, Deringer-Ney manufactures Probes that give probe cards the cost-benefit end customers require: optimizing increased touchdowns over the life of the probe.
Cobra
Cantilever
Straight
Vertical
Cobra Machine
Etching
Manufacturing Probes that give probe cards the cost-benefit end customers require: optimizing increased touchdowns over the life of the probe.
Paliney and Neyoro Family of Alloys
Diameter: 30.5 µm ( 0.0012 inches ) and up
Length: 30mm – 914.4 mm ( 1.1811 – 36 inches )
Foils offer a flexibility other formed products cannot provide. The Deriney Foil is manufactured to meet world class standards in semiconductor and medical applications. These foils are manufactured from the same alloys designed and casted at Deringer-Ney. As for performance, you can expect similar physical and mechanical properties as in wire forms. With thicknesses ranging from 16µm and higher, use for these foils can be found in probe cards, neuro stimulator stints, sensors and industrial applications.
Thickness: 16 µm-100 µm (0.00062 – 0.0039 inches)
Width: 10 cm (3.937 inches)
Length: customer specified
Deringer-Ney is a custom manufacturer of precious metal wire, fine wire, rod, and strip using our world renowned Paliney®, Neyoro™, and Deriney™ alloys. We melt, cast, process, and spool in various tempers and sizes.
Hardness: HK50 400
Elongation: 10%
Elastic Modulus: 135 GPa (19.6 Msi)
UTS: 1240 MPa (180 ksi)
Conductivity: 28% IACS
Resistivity: 6.3 µΩ-cm
Hardness: HK50 260
Elongation: 10%
Elastic Modulus: 117.2 GPa (17 Msi)
UTS: 861 MPa (125 ksi)
Conductivity: 5.5% IACS
Resistivity: 210 Ω-cm
Hardness: HK50 390
Elongation: 3%
Elastic Modulus: 1.20 GPa (17.5 Msi)
UTS: 1,516 MPa (220 ksi)
Conductivity: 14% IACS
Resistivity: 12.3 µΩ-cm