Paliney 6

General Alloy Overview

ASTM

ASTM B563

Application Examples

Industry Examples

Tempers

Annealed
Stress Relieved
Heat Treated

Available Forms

Properties

PropertiesAnnealedStress RelievedHeat Treated
Resistivity, normal, ohm-cmf (Microhm cm )185 (30.7)180 (29.9)155 (25.8)
Conductivity, % IACS, nominal5.65.76.7
Density, Dwt/in3 (grams/cm3)114 (10.8)114 (10.8)114 (10.8)
Solidus Temperature, °F (°C)1890 (1032)1890 (1032)1890 (1032)
Coeff. of Linear Expansion, °F (°C)7.5x106 (13.5x106)7.5x106 (13.5x106)7.5x106 (13.5x106)
Thermal emf vs Platinum, (0-100°C), µV/°C-18--23
Fatigue Strength (Rotating-Bending) at 108 cycles, psi (MPa)--45,000 (310)
Modulus of Elasticity, psi (MPa)16x106 (110x103)16x106 (110x103)16x106 (110x103)
Proportional Limits, psi (MPa)55,000 (380)90,000 (620)110,000 (760)
Ultimate Tensile Strength, psi
  • Wire 0.003-0.020 dia., Rolled Shapes
  • Wire 0.021-0.060 dia
  • Strip 0.003-0.015 thick

100,000-120,000
100,000-120,000
100,000-120,000

135,000-165,000
-
140,000-170,000

150,000-195,000
145,000-190,000
150,000-195,000
Elongation, % in 2 inches
  • Wire 0.003-0.020 dia.
  • Wire 0.021-0.060 dia.
  • Strip 0.003-0.015 thick

20 min
15 min
15 min

8 min
-
8

1-10
1-10
2-10
Knoop Hardness 100 gram load
  • (50 gram under 0.005 thick)
  • Wire 0.003-0.060 dia. Rolled Shapes
  • Strip 0.003-0.015 thick


170-250
170-250


260-330
260-330


320-380
320-380
Knoop Hardness 100 gram load
  • (50 gram under 0.005 thick)
  • Wire 0.003-0.060 dia. Rolled Shapes
  • Strip 0.003-0.015 thick


170-240
170-240


-
-


290-370
330-400