Paliney 2000

General Alloy Overview

ASTM

N/A

Application Examples

Electrical Contacts, Slip Ring Brushes, Low Cost Paliney 7 Replacement

Industry Examples

Industrial, Automotive, Aerospace, and Defense

Tempers

Age Hardened, Annealed, Stress Relieved

Availible Forms

Wire, Strip

Temper Independent Properties

ParameterValueValue 2
Solidus, °F (°C)1615(880)
Liquidus, °F (°C)1760(960)
Melting Range, °F (°C)145(80)
Density, dwt/in³­ (g/cm³)109(10.3)
Specific Heat Capacity, Btu/lb·°F, (J/g·K)0.066(0.28)
Coefficient of Thermal Expansion, /°F (/K)8.9×10-6(1.6×10-5)
Thermal EMF vs Pt, μV/°F (μV/°C)6.3×10-3(1.1×10-2)
Emissivity0.218
ParameterValueValue 2
Thermal Conductivity, Btu/hr·ft·°F (W/m·k)31(54)
Temperature Coefficient of Resistance, /°F (/K)1.2×10-4(2.1×10-4)
Electrical Resistivity, Ω·cmf (µΩ·cm)80.9(13.5)
Electrical Conductivity, %IACS13
Elastic Modulus, Msi (GPa)15(105)
Shear Modulus, Msi (GPa)5.6(38)
Poissons Ratio0.35
Nobility, %29

Temper Dependent Properties

Age Hardened (HT Temper) - Wire - Spool 0.003 - 0.020 in. (0.075 - 0.5 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)†(N/A)
Tensile Elongation to Failure, %1(N/A)
Vickers Microhardness, HV†()
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)170 (1170)150 (1035)
Knoop Microhardness, HK†290

Annealed - Wire - Cut Length 0.003 - 0.020 in. (0.075 - 0.5 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)130 (895)(N/A)
Tensile Elongation to Failure, %11
Vickers Microhardness, HV†(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)130 (895)110 (760)
Knoop Microhardness, HK†200

Stress Relieved - Wire - Spool 0.003 - 0.020 in. (0.075 - 0.5 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)†(N/A)
Tensile Elongation to Failure, %2(N/A)
Vickers Microhardness, HV†(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)175 (1205)150 (1035)
Knoop Microhardness, HK330290

Age Hardened (HT Temper) - Strip 0.003 - 0.020 in. (0.075 - 0.5 mm) thickness

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)†(N/A)
Tensile Elongation to Failure, %31
Vickers Microhardness, HV†(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)150 (1035)130 (895)
Knoop Microhardness, HK330300

Annealed - Strip 0.003 - 0.020 in. (0.075 - 0.5 mm) thickness

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)†(N/A)
Tensile Elongation to Failure, %15(1)
Vickers Microhardness, HV†(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)110 (760)90 (620)
Knoop Microhardness, HK†180