Paliney 6

General Alloy Overview

ASTM

ASTM B563

Application Examples

–

Industry Examples

–

Tempers

Annealed
Stress Relieved
Heat Treated

Available Forms

–

Properties

PropertiesAnnealedStress RelievedHeat Treated
Resistivity, normal, ohm-cmf (Microhm cm )185 (30.7)180 (29.9)155 (25.8)
Conductivity, % IACS, nominal5.65.76.7
Density, Dwt/in3 (grams/cm3)114 (10.8)114 (10.8)114 (10.8)
Solidus Temperature, °F (°C)1890 (1032)1890 (1032)1890 (1032)
Coeff. of Linear Expansion, °F (°C)7.5x106 (13.5x106)7.5x106 (13.5x106)7.5x106 (13.5x106)
Thermal emf vs Platinum, (0-100°C), µV/°C-18--23
Fatigue Strength (Rotating-Bending) at 108 cycles, psi (MPa)--45,000 (310)
Modulus of Elasticity, psi (MPa)16x106 (110x103)16x106 (110x103)16x106 (110x103)
Proportional Limits, psi (MPa)55,000 (380)90,000 (620)110,000 (760)
Ultimate Tensile Strength, psi
  • Wire 0.003-0.020 dia., Rolled Shapes
  • Wire 0.021-0.060 dia
  • Strip 0.003-0.015 thick

100,000-120,000
100,000-120,000
100,000-120,000
135,000-165,000
-
140,000-170,000
150,000-195,000
145,000-190,000
150,000-195,000
Elongation, % in 2 inches
  • Wire 0.003-0.020 dia.
  • Wire 0.021-0.060 dia.
  • Strip 0.003-0.015 thick

20 min
15 min
15 min
8 min
-
8

1-10
1-10
2-10
Knoop Hardness 100 gram load
  • (50 gram under 0.005 thick)
  • Wire 0.003-0.060 dia. Rolled Shapes
  • Strip 0.003-0.015 thick


170-250
170-250

260-330
260-330

320-380
320-380
Knoop Hardness 100 gram load
  • (50 gram under 0.005 thick)
  • Wire 0.003-0.060 dia. Rolled Shapes
  • Strip 0.003-0.015 thick


170-240
170-240

-
-


290-370
330-400

Contact A Specialist

Quick Contact

Global leaders in the invention, development and supply of custom precious metal alloys and precision components. 

353 Woodland Ave
Bloomfield, CT 06002  

Linkedin Youtube

Products

Markets

Capabilities

Resources

Company