Neyoro G

General Alloy Overview

ASTM

ASTM B541

Application Examples

Electrical Contacts

Industry Examples

Automotive, Industrial, Aerospace

Tempers

Age Hardened, Annealed, Wrought Hardened

Availible Forms

Wire, Rod, Strip

Temper Independent Properties

Parameter	Value	Value 2
Solidus, °F (°C)	1700	(925)
Liquidus, °F (°C)	†
Melting Range, °F (°C)	†
Density, dwt/in³ (g/cm³)	170	(15.9)
Specific Heat Capacity, Btu/lb·°F, (J/g·K)	0.049	(0.20)
Coefficient of Thermal Expansion, /°F (/K)	7.0×10^-6	(1.3×10^-5)
Thermal EMF vs Pt, μV/°F (μV/°C)	2.0	(3.5)
Emissivity	†

Parameter	Value	Value 2
Thermal Conductivity, Btu/hr·ft·°F (W/m·k)	26	(48)
Temperature Coefficient of Resistance, /°F (/K)	†
Electrical Resistivity, Ω·cmf (µΩ·cm)	100	(18)
Electrical Conductivity, %IACS	12 (‡)
Elastic Modulus, Msi (GPa)	16	(110)
Shear Modulus, Msi (GPa)	5.5	(38)
Poissons Ratio	0.454
Nobility, %	80

Temper Dependent Properties

Stress Relieved - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	125 (860)	(N/A)
Tensile Elongation to Failure, %	7	5
Vickers Microhardness, HV	†	270

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	145 (1000)	130 (900)
Knoop Microhardness, HK	†	270

Stress Relieved - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	125 (860)	(N/A)
Tensile Elongation to Failure, %	7	4
Vickers Microhardness, HV	†	270

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	145 (1000)	130 (900)
Knoop Microhardness, HK	†	270

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	135 (930)	(N/A)
Tensile Elongation to Failure, %	10	7
Vickers Microhardness, HV	335	285

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	150 (1035)	130 (900)
Knoop Microhardness, HK	330	280

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	135 (930)	(N/A)
Tensile Elongation to Failure, %	10	5
Vickers Microhardness, HV	335	285

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	150 (1035)	130 (900)
Knoop Microhardness, HK	330	270

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	145 (1000)	(N/A)
Tensile Elongation to Failure, %	6	2
Vickers Microhardness, HV	†	290

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	180 (1250)	150 (1035)
Knoop Microhardness, HK	350	310

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	145 (1000)	(N/A)
Tensile Elongation to Failure, %	6	2
Vickers Microhardness, HV	†	290

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	180 (1250)	145 (1000)
Knoop Microhardness, HK	†	290

Annealed - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	†	(N/A)
Tensile Elongation to Failure, %	25	20
Vickers Microhardness, HV	†	180

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	95 (650)	80 (550)
Knoop Microhardness, HK	225	180

Annealed - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	†	(N/A)
Tensile Elongation to Failure, %	25	16
Vickers Microhardness, HV	†	180

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	95 (655)	85 (585)
Knoop Microhardness, HK	225	180

Age Hardened From Solution Annealed
(HT-A Temper) - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	†	(N/A)
Tensile Elongation to Failure, %	9	4
Vickers Microhardness, HV	†	285

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	145 (1000)	130 (900)
Knoop Microhardness, HK	330	270

Annealed - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	†	(N/A)
Tensile Elongation to Failure, %	25	7
Vickers Microhardness, HV	†	180

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	100 (690)	80 (550)
Knoop Microhardness, HK	†	180

Stress Relieved - Strip 0.003 - 0.020 in. (0.075 - 0.5 mm) thickness

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	110 (760)	(N/A)
Tensile Elongation to Failure, %	7	3
Vickers Microhardness, HV	†	270

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	130 (900)	125 (860)
Knoop Microhardness, HK	†	270

Age Hardened From Solution Annealed
(HT-A Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	125 (860)	(N/A)
Tensile Elongation to Failure, %	9	3
Vickers Microhardness, HV	†	275

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	145 (1000)	125 (860)
Knoop Microhardness, HK	325	270

Age Hardened From Solution
Annealed and Cold-Worked
(HTCW Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	†	(N/A)
Tensile Elongation to Failure, %	3	2
Vickers Microhardness, HV	†	285

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	170 (1170)	140 (965)
Knoop Microhardness, HK	350	290

Annealed - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Parameter	Nominal	Min
	Nominal	Min
0.2% Offset Yield Strength, ksi (MPa)	90 (620)	(N/A)
Tensile Elongation to Failure, %	20	12
Vickers Microhardness, HV	†	180

Parameter	Nominal	Min
	Nominal	Min
Ultimate Tensile Strength, ksi (MPa)	110 (760)	85 (585)
Knoop Microhardness, HK	230	200

† - Values containing † are available upon request

‡ - Values containing (‡) only apply to age hardened conditions

Contact A Specialist

Quick Contact

First Name

Last Name

Phone Number

Country

City

State

Zip

Market

Interest

Please tell us about your needs. Be as specific as possible.

File Upload

Choose File

I consent to have this website store my submitted information so they can respond to my inquiry

Cookie	Duration	Description
cookielawinfo-checkbox-analytics	11 months	This cookie is set by GDPR Cookie Consent plugin. The cookie is used to store the user consent for the cookies in the category "Analytics".
cookielawinfo-checkbox-functional	11 months	The cookie is set by GDPR cookie consent to record the user consent for the cookies in the category "Functional".
cookielawinfo-checkbox-necessary	11 months	This cookie is set by GDPR Cookie Consent plugin. The cookies is used to store the user consent for the cookies in the category "Necessary".
cookielawinfo-checkbox-others	11 months	This cookie is set by GDPR Cookie Consent plugin. The cookie is used to store the user consent for the cookies in the category "Other.
cookielawinfo-checkbox-performance	11 months	This cookie is set by GDPR Cookie Consent plugin. The cookie is used to store the user consent for the cookies in the category "Performance".
viewed_cookie_policy	11 months	The cookie is set by the GDPR Cookie Consent plugin and is used to store whether or not user has consented to the use of cookies. It does not store any personal data.

Neyoro G

General Alloy Overview

ASTM

Application Examples

Industry Examples

Tempers

Availible Forms

Temper Independent Properties

Temper Dependent Properties

Stress Relieved - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Stress Relieved - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Annealed - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Annealed - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Annealed - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Stress Relieved - Strip 0.003 - 0.020 in. (0.075 - 0.5 mm) thickness

Age Hardened From Solution Annealed
(HT-A Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Age Hardened From Solution
Annealed and Cold-Worked
(HTCW Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Annealed - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

† - Values containing † are available upon request

‡ - Values containing (‡) only apply to age hardened conditions

Contact A Specialist

Products

Markets

Capabilities

Resources

Company

Neyoro G

General Alloy Overview

ASTM

Application Examples

Industry Examples

Tempers

Availible Forms

Temper Independent Properties

Temper Dependent Properties

Stress Relieved - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Stress Relieved - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Age Hardened From Solution Annealed (HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed (HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed and Cold-Worked(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed and Cold-Worked(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Annealed - Wire - Spool 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Annealed - Wire - Spool 0.020 - 0.080 in. (0.5 - 2.0 mm) diameter

Age Hardened From Solution Annealed (HT-A Temper) - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Annealed - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Stress Relieved - Strip 0.003 - 0.020 in. (0.075 - 0.5 mm) thickness

Age Hardened From Solution Annealed (HT-A Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Age Hardened From Solution Annealed and Cold-Worked (HTCW Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Annealed - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

† - Values containing † are available upon request

‡ - Values containing (‡) only apply to age hardened conditions

Contact A Specialist

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution
Annealed and Cold-Worked
(HT-CW Temper) - Wire - Cut Length 0.004 - 0.020 in. (0.1 - 0.5 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Rod 0.081 - 0.187 in. (2.1 - 4.75 mm) diameter

Age Hardened From Solution Annealed
(HT-A Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness

Age Hardened From Solution
Annealed and Cold-Worked
(HTCW Temper) - Strip 0.002 - 0.050 in. (0.05 - 1.25 mm) thickness