Deriney 72

General Alloy Overview

ASTM

N/A

Application Examples

Medical Devices

Industry Examples

Medical

Tempers

Age Hardened, Annealed, Wrought Hardened

Availible Forms

Wire, Strip

Temper Independent Properties

ParameterValueValue 2
Solidus, °F (°C)2830(1555)
Liquidus, °F (°C)5870(1575)
Melting Range, °F (°C)40(20)
Density, dwt/in³­ (g/cm³)175(16.4)
Specific Heat Capacity, Btu/lb·°F, (J/g·K)0.05(0.20)
Coefficient of Thermal Expansion, /°F (/K)6.7×10-6(1.2×10-5)
Thermal EMF vs Pt, μV/°F (μV/°C)14.8(26.7)
Emissivity0.368
ParameterValueValue 2
Thermal Conductivity, Btu/hr·ft·°F (W/m·k)8.4(15)
Temperature Coefficient of Resistance, /°F (/K)3.3×10-4(6.0×10-4)
Electrical Resistivity, Ω·cmf (µΩ·cm)300(50)
Electrical Conductivity, %IACS3.5
Elastic Modulus, Msi (GPa)29.6(205)
Shear Modulus, Msi (GPa)10.8(74.8)
Poissons Ratio0.363
Nobility, %78.2

Temper Dependent Properties

Annealed - Wire - Spool 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)165 (1140)(N/A)
Tensile Elongation to Failure, %13(N/A)
Vickers Microhardness, HV330(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)205 (1410)(N/A)
Knoop Microhardness, HK335(N/A)

Stress Relieved - Wire - Spool 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)250 (1700)(N/A)
Tensile Elongation to Failure, %1(N/A)
Vickers Microhardness, HV445(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)285 (1950)(N/A)
Knoop Microhardness, HK455(N/A)

Cold Worked (CW<70% AR Temper) - Wire - Cut Length 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)200 (1380)(N/A)
Tensile Elongation to Failure, %3(N/A)
Vickers Microhardness, HV480(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)230 (1580)(N/A)
Knoop Microhardness, HK490(N/A)

Cold Worked (CW>70% AR Temper) - Wire - Cut Length 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)310 (2140)(N/A)
Tensile Elongation to Failure, %2(N/A)
Vickers Microhardness, HV520(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)330 (2270)(N/A)
Knoop Microhardness, HK335(N/A)

Age Hardened (HTCW<70% AR Temper) - Wire - Spool 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)245 (1690)(N/A)
Tensile Elongation to Failure, %2(N/A)
Vickers Microhardness, HV615(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)250 (1720)(N/A)
Knoop Microhardness, HK625(N/A)

Age Hardened (HTCW>70% AR Temper) - Wire - Spool 0.002 - 0.080 in. (0.05 - 2.0 mm) diameter

ParameterNominalMin
NominalMin
0.2% Offset Yield Strength, ksi (MPa)245 (1140)(N/A)
Tensile Elongation to Failure, %2(N/A)
Vickers Microhardness, HV520(N/A)
ParameterNominalMin
NominalMin
Ultimate Tensile Strength, ksi (MPa)250 (1720)(N/A)
Knoop Microhardness, HK530(N/A)

† - Values containing † are available upon request​